Effect of zirconia surface treatment on zirconia/veneer interfacial toughness evaluated by fracture mechanics method

Wang, GaoqiZhang, SongBian, CuirongKong, Hui

Journal:JOURNAL OF DENTISTRY

Abstract:

Objectives: The aim of this study was to evaluate the effect of the airborne-particle abrasion and liner application on the interfacial toughness between veneering porcelain and zirconia core by means of a fracture mechanics test.

Methods: Beam-shaped zirconia specimens were sectioned and divided into 4 groups according to different surface treatments as follows: Group C (control): no treatment; Group L: application of liner; Group A: airborne-particle abrasion with Al2O3 (sandblasting); and Group AL: airborne-particle abrasion and application of liner. The zirconia surfaces before and after sandblasting were observed and analyzed by SEM and white light interferometer. Specimens of each pretreated group were veneered with 3 core/veneer thickness ratios of 2:3, 1:1, and 3:2, corresponding to 3 phase angles respectively. Fracture mechanics test was performed on each specimen, the energy release rate G and phase angle psi were calculated to characterize interfacial toughness. The experimental data were analyzed statistically using three-way ANOVA and the Tukey's HSD test. The surfaces of fractured specimens were examined by SEM and EDX.

Results: At each phase angle, the interfaces with no treatment had higher mean G values than that of other groups. All the specimens showed mixed failure mode with residual veneer or liner on the zirconia surfaces.

Conclusions: The toughness of zirconia/veneer interface with no treatment is significantly higher than that of interfaces subjected to liner application and airborne-particle abrasion.

Clinical significance: Liner application and airborne-particle abrasion seem to reduce zirconia/veneer interfacial toughness. Therefore, the two surface treatment methods should be applied with caution. (C) 2014 Elsevier Ltd. All rights reserved.

Keywords:

Bilayer; Airborne-particle abrasion; Liner; Interfacial toughness

Download:

Effect of zirconia surface treatment on zirconia/veneer interfacial toughness evaluated by fracture mechanics method 》

教育部直属高校 国家“985”工程 “211”工程 “双一流”重点建设本科大学

 Copyright© 2015 All Rights Reserved. 高校网站模板版权所有  京ICP备15000288 号